Abstract:  Development of a novel high performing inorganic p‐type thin film transistor could pave the way for new transparent electronic devices. This complements the widely commercialized n‐type counterparts, indium‐gallium‐zinc‐oxide (IGZO). Of the few potential candidates, copper monoiodide (CuI) stands out. It boasts visible light transparency and high intrinsic hole mobility (>40 cm2 V−1 s−1), and is suitable for various low‐temperature processes. However, the performance of reported CuI transistors is still below expected mobility, mainly due to the uncontrolled excess charge‐ and defect‐scattering from thermodynamically favored formation of copper and iodine vacancies. Here, a solution‐processed CuI transistor with a significantly improved mobility is reported. This enhancement is achieved through a room‐temperature vacancy‐engineering processing strategy on high‐k dielectrics, sodium‐embedded alumina. A thorough set of chemical, structural, optical, and electrical analyses elucidates the processing‐dependent vacancy‐modulation and its corresponding transport mechanism in CuI. This encompasses defect‐ and phonon‐scattering, as well as the delocalization of charges in crystalline domains. As a result, the optimized CuI thin film transistors exhibit exceptionally high hole mobility of 21.6 ± 4.5 cm2 V−1 s−1. Further, the successful operation of IGZO‐CuI complementary logic gates confirms the applicability of the device.

논문정보:  Advanced Materials, 35(51), 2307206
Published:  December 21, 2023
DOI:  doi.org/10.1002/adma.202307206